No Clean Rosin Liquid Flux Light Yellow Clear Liquid Acid Flux Transparent

Rosin-type flux  no-clean flux  light yellow  clear and transparent liquid

1.  Introduction
◆ NS319  is a no-clean flux with medium solid content (5.0% solid content), halogen-free and high activity. It can be used in foaming, spraying and other forms.
◆ Resin active system has excellent wettability on the surface of bare copper and solder layer.
◆ The welding of multi-layer boards with metallized small holes will show excellent penetration performance.
◆ There are very few residues on the PCB surface after soldering, and the solder joints are uniform and bright and full and can be tested without cleaning.

2.  Instructions for use
◆ In order to meet the requirements of stable soldering performance and electrical performance reliability, the process establishment related to circuit boards and components must meet the requirements of solderability and ion clarity. It is recommended that the assembler put forward relevant regulations for the supplier of related materials, and require the incoming material analysis certificate or the assembler to carry out incoming material inspection.
◆ When assembling, handle the circuit board carefully. Only grasp the edge of the circuit board. It is recommended to use clean, lint-free gloves.
◆ Use FD5050 thinner to regularly clean the conveyor belt, chain teeth and clamps, which can avoid the increase of residues on the edge of the circuit board after assembly.
◆ When changing the type of flux, use FD5050 thinner to thoroughly clean the flux container, flux tank, flux spray system, etc.
◆ The density and uniformity of the flux coating are critical to the successful application of no-clean fluxes. It is recommended to use flux coatings with a density of 500 to 1500 micrograms per square inch.

◆ Preheating makes the flux on the circuit board dry, enhancing the removal of oxides and the formation of good solder joints. The preheating temperature depends on various factors, such as conveyor speed, types of devices and substrates.
◆ Using compressed air with degreasing and dewatering when foaming coating is used to foam, so that enough flux is maintained on the foam core. Use a pressure regulator to adjust the air pressure to produce uniform bubbles and optimal height.
◆ The flux applicator needs to add a thinner to supplement the evaporation loss and maintain the balance of the flux composition.
◆ Debris and contaminants will accumulate in the circulating flux coating. For the consistency of the soldering operation, the no longer used flux should be disposed of regularly. After emptying the flux, use the thinner to clean the container and other tasks, and then fill the container with fresh flux. The flux should be given a few minutes to stabilize before the soldering can be resumed.

3.storage method
◆ Store in a cool, dry, well-ventilated place or a dangerous goods warehouse that cannot be directly exposed to sunlight.
◆ The work area should have a "No Pyrotechnics" sign.
◆ The storage area should be clearly marked, and designated or trained personnel are allowed to enter.
◆ There may still be residues in the empty barrels and pipelines, and heat treatment must be carried out before cleaning.
◆ Use a ventilation system that does not produce sparks.
◆ Ensure that the packaging is intact to avoid the accumulation and damage of the container.
◆ This product is packaged in plastic barrels with a storage period of one year. It is transported and packaged as dangerous goods.